High quality Insulating Curing Banding Tape
It should be processed with an appropriate winding device. Winding takes place a room temperature, or when heated up, via pre-heater rotor, optionally with infrared radiators. Due to warm winding , a residual voltage of approximately 60% of the applied tensile force is achieve in the bandage. After winding and selective fixation (infrared radiator or soldering gun) the resin has to be polymerized in the oven according to the hardness stated in the table.
It is used for banding electrical machines, coils and other electronic equipment, Advantages in comparison to steel bandages:
- Eddy current free material and thus no local overheating.
- No fatigue fractures
- Resistance to corrosion in tropical environments
- Reduction of process cost due to short processing time
- Reduction of insulating material and weight
mm mm 10 15 20 25 30 50
Pancake meters: 200 200 200 200 200 100/160
Spool meters: 800 500 1800 1500 1200
Under special request we can deliver in 100 meters length
|
Product Name: |
Glass Banding Tape |
Raw Material: |
Resin, Glass Fibre |
|
Color: |
White |
Thermal Class： |
H Class, 200℃ |
|
Dielectric strength： |
≥ 12 KV |
Thickness: |
10mm,15mm,20mm,25mm, 30mm,50mm |
|
Industrial Use: |
Used in Motor |
Origin: |
HangZhou Zhejiang |
|
Packing: |
Standard Export Packaging |
||
Insulating Curing Banding Tape Glass Banding Tape VITROGLASS Resin Glass Banding Tape Glass Fiber Banding Tape
Insulating Curing Banding Tape | Glass Banding Tape | Resin Glass Banding Tape | Glass Fiber Banding Tape | VITROGLASS
|
Place of Origin |
China |
|
Brand name |
HangZhou Times |
|
Certification |
ISO9001, ROHS, REACH |
|
Glass Banding Tape |
|
|
Minimum Order Quantity |
10000 M |
|
Price（usd） |
0.07 ~0.3 / M |
|
Packaging Details |
Normal Export Packaging |
|
Supply Ability |
500000 M / day |
|
Delivery Port |
Shanghai / Ningbo |
|
Color |
White |
|
Material |
Resin, Glass Fibre |
|
Thermal class |
Class F (155ºC) |
Class H (200ºC) |
Standards |
||
|
Thickness |
mm |
0.20 ± 0,03 |
0.20 ± 0,03 |
GB/T 22471.2 |
|
|
0.30± 0,03 |
0.30± 0,03 |
||||
|
Loss of weight at calcination |
% |
26±2 |
26±2 |
GB/T 22471.2 |
|
|
Volatile content |
% |
≤2 |
≤2 |
GB/T 22471.2 |
|
|
Tensile Strength before curing |
0.20mm |
N/cm |
≥1000 |
≥1200 |
GB/T 22471.2 |
|
0.30mm |
N/cm |
≥1500 |
≥2000 |
||
|
Maximum pull while banding |
0.20mm |
N/cm |
≥500 |
≥600 |
GB/T 22471.2 |
|
Storage temperature and storage live
|
At 10ºC |
Months |
20 |
24 |
|
At 15ºC |
Months |
15 |
18 |
|
|
At 20ºC |
Months |
10 |
12 |
|
|
At 30ºC |
Months |
6 |
8 |
|
ELECTRICAL |
unit |
Class F |
Class H |
Standards |
|
Dielectric Strength |
KV/mm |
≥12 |
≥12 |
GB/T 22471.2 |
|
Arc resistance |
S |
≥160 |
≥160 |
GB/T 22471.2 |
|
Proof tracking index |
V |
≥500 |
≥500 |
GB/T 22471.2 |